Microstructure,tribological behavior and magnetic properties of Fe−Ni−TiO2 composite coatings synthesized via pulse frequency variation

The Fe−Ni−TiO₂ nanocomposite coatings were electrodeposited by pulse frequency variation. The results showed that the nanocomposite with a very dense coating surface and a nanocrystalline structure was produced at higher frequencies. By increasing the pulse frequency from 10 to 500 Hz, the iron and TiO₂ nanoparticles contentswere increased in expense of nickel content. XRD patterns showed that by increasing the frequency to 500 Hz, an enhancement ofBCC phase was observed and the grain size of deposits was reduced to 35 nm. The microhardness and the surface roughness were increased to 647 HV and 125 nm at 500 Hz due to the grain size reduction and higher incorporation of TiO₂ nanoparticles into the Fe−Ni matrix (5.13 wt.%). Moreover, the friction coefficient and wear rate values were decreased by increasing the pulse frequency;while the saturation magnetization and coercivity values of the composite deposits were increased.     

Probing the degenerate pattern growth of {100}<011> orientation in a directionally solidified Al-4.5 wt% Cu alloy

Degenerate pattern is a seemingly disordered morphology but it exhibits the inherently ordered crystal connected with tip-splitting and limited stability which makes it difficult to observe in the metallic system. Here we employ (100)[011] orientated planar-front seeds using directional solidification and reveal the fundamental origins of the degenerate pattern growth in an Al-4.5 wt% Cu alloy. We find that the spacing of the tip-splitting (λ) in the degenerate of the alloys followed a power law, λ∝V^−0.5, and the frequency (f) of the splitting was related to the growth velocity (V) by ƒ∝V^1.5. The dimensionless growth direction (θ/θ₀) increased monotonously and approached 0.6 with faster velocity, attributed to its anisotropy in the interface kinetics. Once growth velocity exceeded a threshold, two types of pattern transitions from degenerate to regular dendrites were proposed. One of them exhibited a random and chaotic mode and the other underwent a rotation in growth direction.     

轧制与退火对T9S钛合金板材组织与性能的影响

研究了轧制变形量及退火温度对T9S钛合金板材显微组织和室温力学性能的影响。结果表明:增加成品轧制变形量,板材组织破碎更充分,退火后形成等轴α相、拉长α相和晶间β相组织形貌,变形流线比较明显,板材室温强度和硬度升高,伸长率降低,弹性模量增加。随着退火温度升高,板材室温强度和硬度逐渐降低,伸长率逐渐提高,横向弹性模量逐渐减小,纵向弹性模量先增加后减小。经(750~790) ℃×45 min空冷退火处理后的板材可以获得较好的强度和塑性的匹配。     

Fe基非晶合金增强1060铝基多层复合材料的组织与性能

采用累积叠轧焊+中间退火法复合轧制1060Al/Fe基非晶多层铝合金复合板材。利用光学显微镜、扫描电镜、X-衍射分析仪以及拉伸试验机分析Al基复合材料的微观组织结构变化、断口形貌、物相组成以及力学性能。结果表明:Fe基非晶复合材料的增强体在300 ℃中间退火过程中发生部分晶化,在累积变形轧制过程中发生破碎,并随着变形道次的增加,破碎程度随之增大;复合板前6道次的累积轧制变形出现了明显的加工软化现象,并且随着变形道次的增加,其加工软化的效果愈明显;随着累积轧制变形道次增加,Al基复合材料的力学性能发生了明显的变化,第2道次轧制变形后屈服强度与抗拉强度达到了最大值为140 MPa和156 MPa,伸长率为5.53%,达到最佳综合性能。     

退火工艺对激光选区熔化成形Ti6Al4V合金组织及室温力学性能的影响

以Ti6Al4V球形粉末为原料,利用激光选区熔化成形方法制备了Ti6Al4V合金试样,采用光学显微镜、扫描电镜及力学性能测试等手段,研究了退火工艺对Ti6Al4V合金室温力学性能及组织的影响规律。结果表明: SLM成形沉积态Ti6Al4V合金室温抗拉强度超过1200 MPa,而平均断后伸长率仅为4.0%;在650 ℃下进行真空退火处理,合金的抗拉强度仍保持在1200 MPa左右,规定塑性延伸强度R_p0.2高于1150 MPa,但试样的断后伸长率<10%;而在750及800 ℃下进行真空退火处理,合金试样的抗拉强度降至1100 MPa左右,规定塑性延伸强度高于1050 MPa,伸长率达到甚至超过10%,材料的综合强韧性得到明显提升。随着真空退火加热温度和保温时间的增加,SLM成形Ti6Al4V合金原始β晶界逐渐变模糊,晶粒趋向于等轴化。与此同时,快速冷却转变的α′针状马氏体未出现明显地粗化。     

Influence of Bridgman solidification on microstructures and magnetic behaviors of a non-equiatomic FeCoNiAlSi high-entropy alloy

The non-equiatomic FeCoNiAlSi alloy is prepared by the Bridgman solidification (BS) technique at different withdrawal velocities (V = 30, 100, and 200 μm/s). Various characterization techniques have been used to study the microstructure and crystal orientation. The morphological evolutions accompanying the crystal growth of the alloy prepared at different withdrawal velocities are nearly the same, from equiaxed grains to columnar crystals. The transition of coercivity is closely related to the local microstructure, while the saturation magnetization changes little at different sites. The coercivity can be significantly reduced from the equiaxed grain area to the columnar crystal area when the applied magnetic field direction is parallel to the crystal growth direction, no matter what is the withdrawal velocity. In addition, the alloy possesses magnetic anisotropy when the applied magnetic field is in different directions.     

Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

Low cycle fatigue behavior of a eutectic 80Au/20Sn solder alloy

The eutectic 80Au/20Sn solder alloy is widely used in high power electronics and optoelectronics packaging. In this study, low cycle fatigue behavior of a eutectic 80Au/20Sn solder alloy is reported. The 80Au/20Sn solder shows a quasi-static fracture characteristic at high strain rates, and then gradually transforms from a transgranular fracture (dominated by fatigue damage) to intergranular fracture (dominated by creep damage) at low strain rates with increasing temperature. Coffin-Manson and Morrow models are proposed to evaluate the low cycle fatigue behavior of the 80Au/20Sn solder. Besides, the 80Au/20Sn solder has enhanced fatigue resistance compared to the 63Sn/37Pb solder.     

高强WSTi544221合金组织与性能研究

研究了轧制变形量对WSTi544221合金棒材显微组织和力学性能的影响,并对Φ10 mm规格的棒材进行不同制度的固溶+时效处理,对比了不同热处理状态下棒材的组织和力学性能。结果表明,随着轧制变形量的增大,WSTi544221合金棒材的晶粒细化程度增大,强度逐渐提高,但塑性变化不大。经870℃×1 h/WC+520℃×6 h/AC固溶+时效处理后,强度与塑性可以获得良好匹配,当抗拉强度达到1 610 MPa、屈服强度达到1 531 MPa时,延伸率和断面收缩率可分别保持在12%和43%。     

钛合金表面多磁极耦合旋转磁场光整加工特性

面向激光增材制造钛合金表面的光整加工需求，设计出一种多磁极耦合旋转磁场光整加工装置来研究光整加工特性。基于ANSYS Maxwell仿真软件分析了光整加工装置的磁场强度分布。搭建了实验光整平台，分析了主轴转速、C轴转速和加工间隙对表面质量的影响。结果表明，在主轴转速500 r/min、C轴转速160 r/min和加工间隙0.7 mm的加工条件下，表面粗糙度Ra由5.991 μm下降至0793 μm。扫描电子显微镜(SEM)观测表明，光整后的钛合金表面沉积层消失，表面质量得到显著改善。